... presented approximately the same final weld metal oxygen contents it is reasonable to assume that their kinetics of oxygen absorption were similar . That is , from the electrode tip until the final solidification of the pool , these two ...
... presented approximately the same final weld metal oxygen contents it is reasonable to assume that their kinetics of oxygen absorption were similar . That is , from the electrode tip until the final solidification of the pool , these two ...
Page 214
... presented in [ 15 ] . Whilst the experimental investigations yield information on the collapse load , two different types of result are obtained from the numerical investigations performed on cracked tubular joints [ 9 - 14 ] , i.e. ...
... presented in [ 15 ] . Whilst the experimental investigations yield information on the collapse load , two different types of result are obtained from the numerical investigations performed on cracked tubular joints [ 9 - 14 ] , i.e. ...
Page 498
... presented in Fig.7 ( a ) and 7 ( b ) respectively . The rate of surface crack extension in the chord shows a small deceleration , as does the rate of depth extension . In common with other specimens with stiffening in the saddle region ...
... presented in Fig.7 ( a ) and 7 ( b ) respectively . The rate of surface crack extension in the chord shows a small deceleration , as does the rate of depth extension . In common with other specimens with stiffening in the saddle region ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength