Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 70
Page 111
DESIGNING THE REPAIR AWEC , ARC and Global collaborated in designing the horizontal member repair assembly . AWEC's objective was to restore the structure to its original design strength . This required installing the new assembly in ...
DESIGNING THE REPAIR AWEC , ARC and Global collaborated in designing the horizontal member repair assembly . AWEC's objective was to restore the structure to its original design strength . This required installing the new assembly in ...
Page 236
... repair condition which considers the findings of inspections carried out on the initially fabricated welds prior to any repairs , the post - repair phase which considers the findings of inspections made on repaired welds , the combined ...
... repair condition which considers the findings of inspections carried out on the initially fabricated welds prior to any repairs , the post - repair phase which considers the findings of inspections made on repaired welds , the combined ...
Page 383
... repair welded wideplates notched at the original weld deposit , repair weld and HAZ regions are discussed . The aim of this work was to investigate the effects of strength mis - match and notch position on the fracture performance of ...
... repair welded wideplates notched at the original weld deposit , repair weld and HAZ regions are discussed . The aim of this work was to investigate the effects of strength mis - match and notch position on the fracture performance of ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength