Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 85
Page 152
... temperature . In some cases ( Hippsley et al . , 1982 ) specimens were first stressed at room temperature and then heated slowly to simulate a post - weld stress - relief heat treatment . In other cases ( Ritter and McPherson , 1974 ) ...
... temperature . In some cases ( Hippsley et al . , 1982 ) specimens were first stressed at room temperature and then heated slowly to simulate a post - weld stress - relief heat treatment . In other cases ( Ritter and McPherson , 1974 ) ...
Page 206
... temperature to evaluate the statistical characteristic of the critical CTOD at each temperature point . Figure 5 presents the test results of CTOD of welded joint at five temperatures , the relationship between CTOD and temperature ...
... temperature to evaluate the statistical characteristic of the critical CTOD at each temperature point . Figure 5 presents the test results of CTOD of welded joint at five temperatures , the relationship between CTOD and temperature ...
Page 290
... temperature . This could mean a nominal tempera- ture below 600 ° C . For example , BS7191 ' recommends that Grade 450 steel is PWHT within the temperature range 550-620 ° C . For C - Mn steels , the AWS D1.1 code ( 1994 ) requires PWHT ...
... temperature . This could mean a nominal tempera- ture below 600 ° C . For example , BS7191 ' recommends that Grade 450 steel is PWHT within the temperature range 550-620 ° C . For C - Mn steels , the AWS D1.1 code ( 1994 ) requires PWHT ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength