... Tensile Tests The all - weld - metal tensile test data for the ferritic steel vertical butt welds are presented in Fig.5 ( a ) , as a function of IIW CE . Yield strength values ranged from 385 and 395 MPa for weld D / B / V to 495 and ...
... Tensile Tests The all - weld - metal tensile test data for the ferritic steel vertical butt welds are presented in Fig.5 ( a ) , as a function of IIW CE . Yield strength values ranged from 385 and 395 MPa for weld D / B / V to 495 and ...
Page 258
... Tensile tests were conducted on the 12 , 8 , and 4 ply hybrid laminates to provide data for comparison to the analytical efforts . A summary of the tensile test results is presented in Table I. Analysis of variance ( ANOVA ) tables were ...
... Tensile tests were conducted on the 12 , 8 , and 4 ply hybrid laminates to provide data for comparison to the analytical efforts . A summary of the tensile test results is presented in Table I. Analysis of variance ( ANOVA ) tables were ...
Page 412
... Tensile tests 0 - 50 % cold - rolling of AISI 304LN steel increased yield strength gradually from 314 to 1005 MPa in room temperature tensile tests . The corresponding increase in tensile strength was from 624 to 1158 MPa ( Fig . 3 ) ...
... Tensile tests 0 - 50 % cold - rolling of AISI 304LN steel increased yield strength gradually from 314 to 1005 MPa in room temperature tensile tests . The corresponding increase in tensile strength was from 624 to 1158 MPa ( Fig . 3 ) ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses ring riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength