Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 72
Page 81
TUBE THICKNESS INFLUENCE IN THE SHEET / TUBE JOINT DEFORMATION OBTAINED BY ELECTRICAL RESISTANCE SPOT WELDING Itamar Ferreira Department of Materials Campinas State University Campinas , São Paulo , Brazil I HYDROGEN CONTENT OF ...
TUBE THICKNESS INFLUENCE IN THE SHEET / TUBE JOINT DEFORMATION OBTAINED BY ELECTRICAL RESISTANCE SPOT WELDING Itamar Ferreira Department of Materials Campinas State University Campinas , São Paulo , Brazil I HYDROGEN CONTENT OF ...
Page 446
... thickness 0.20 T 1 OPB Through thickness 0.19 T 0.50 10.20 0.96 3 Axial tension Through thickness 0.20 , 0.26 , 0.33 T 2 Axial tension Surface 0.20 0.25T , 0.50T 2 OPB Through thickness 0.20 , 0.25 T 2 OPB Surface 0.20 , 0.20 0.25T ...
... thickness 0.20 T 1 OPB Through thickness 0.19 T 0.50 10.20 0.96 3 Axial tension Through thickness 0.20 , 0.26 , 0.33 T 2 Axial tension Surface 0.20 0.25T , 0.50T 2 OPB Through thickness 0.20 , 0.25 T 2 OPB Surface 0.20 , 0.20 0.25T ...
Page 517
... thickness of 16mm . A thickness effect factor that accounts for the general reduction of fatigue life with increasing material thickness has been introduced as a modifier to the stress used in the S - N curves . The general form of the ...
... thickness of 16mm . A thickness effect factor that accounts for the general reduction of fatigue life with increasing material thickness has been introduced as a modifier to the stress used in the S - N curves . The general form of the ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength