Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 27
Page 198
... wide plate was predicted from the 3 - point bend CTÖD results . Figure 10 presents the estimation procedure based on ... plates is shown in Fig . 11 together with the experimental results . It is found that the conventional CTOD concept ...
... wide plate was predicted from the 3 - point bend CTÖD results . Figure 10 presents the estimation procedure based on ... plates is shown in Fig . 11 together with the experimental results . It is found that the conventional CTOD concept ...
Page 199
... wide plate was derived finally . Figure 15 presents the critical overall strain ( _ ) , of the wide plates predicted by the local approach . Compared to the conventional CTOD concept , the local approach gives more reasonable prediction ...
... wide plate was derived finally . Figure 15 presents the critical overall strain ( _ ) , of the wide plates predicted by the local approach . Compared to the conventional CTOD concept , the local approach gives more reasonable prediction ...
Page 385
The wide plates ( total length of 1580 mm ) were prepared by welding of two head pieces to the original weld plates ... plate exhibits significantly . lower CTOD than the wide plate without repair for the 385.
The wide plates ( total length of 1580 mm ) were prepared by welding of two head pieces to the original weld plates ... plate exhibits significantly . lower CTOD than the wide plate without repair for the 385.
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength