Page 469
... grade In Figure 7 is shown SN data for welds in pipe of ASTM Grade 28 and 29 respectively , 1G welds . It is observed that that the lower strength Grade 28 has slightly lower fatigue strength . However , the difference is small , and ...
... grade In Figure 7 is shown SN data for welds in pipe of ASTM Grade 28 and 29 respectively , 1G welds . It is observed that that the lower strength Grade 28 has slightly lower fatigue strength . However , the difference is small , and ...
Page 494
... grades were included in the test : Grade 23 , Grade 23 + Pd , Grade 29 ( 23 + Ru ) , Grade 9 , Grade 9M and SuperTIX . The composition is shown in Table 1. The mechanical properties are given in Table 2. Grade 23 , Grade 23 + Pd and Grade ...
... grades were included in the test : Grade 23 , Grade 23 + Pd , Grade 29 ( 23 + Ru ) , Grade 9 , Grade 9M and SuperTIX . The composition is shown in Table 1. The mechanical properties are given in Table 2. Grade 23 , Grade 23 + Pd and Grade ...
Page 496
... Grade 23 51 94 25 89 Grade 29 ( Ru ) 16 97 97 125 129 151 96 148 83 134 85 110 Grade 9 10 82 50 57 89 43 76 39 52 31 42 Grade 9M 77 86 77 25 88 Grade 23+ Pd 24 127 98❘ 86 151 97 62 SuperTIX 66 77 Grade 5 115 Grade 29 Weld 131 Grade 29 ...
... Grade 23 51 94 25 89 Grade 29 ( Ru ) 16 97 97 125 129 151 96 148 83 134 85 110 Grade 9 10 82 50 57 89 43 76 39 52 31 42 Grade 9M 77 86 77 25 88 Grade 23+ Pd 24 127 98❘ 86 151 97 62 SuperTIX 66 77 Grade 5 115 Grade 29 Weld 131 Grade 29 ...
Other editions - View all
Common terms and phrases
alloys analysis applied approximately assessment bending calculated carried coating compared composite compressive considered corrosion crack crack growth curve cycles damage defect deformation depth determined developed direction distribution effect element Engineering equation estimated evaluation experience factor failure fatigue field Figure flaw flexible fracture function geometry given Grade heat higher hydrogen important increase initial installation insulation integrity International joint length limit load locations lower material maximum mean measured mechanical method observed obtained Offshore operation parameters performed pipe plate predicted present pressure problem procedure production properties range reliability residual resistance respectively riser rope safety samples shown shows side simulation solution specimens standard steel strain strength stress structure surface Table temperature tensile tension thermal thickness titanium toughness uncertainties variables weld