Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2002 - Arctic regions |
From inside the book
Results 1-3 of 85
Page 182
... bending radius . The deformability was calculated for both the opening mode and closing mode . The geometric parameters of the ' bend part ' were the imperfections of the bending angle , the bending radius , the ovality and the wall ...
... bending radius . The deformability was calculated for both the opening mode and closing mode . The geometric parameters of the ' bend part ' were the imperfections of the bending angle , the bending radius , the ovality and the wall ...
Page 189
... bending were experimentally and analytically investigated . Full - scale cold bending experiments were performed on API X60 and X80 grade line pipes . The reduction in the yield stress of the cold bends due to the Bauschinger effect was ...
... bending were experimentally and analytically investigated . Full - scale cold bending experiments were performed on API X60 and X80 grade line pipes . The reduction in the yield stress of the cold bends due to the Bauschinger effect was ...
Page 190
... bending CRC - Evans PB12-16 and PB22-36 type bending machines were used for Pipes A and B , respectively . Figure 3 is an illustration of the bending machines . The bending machine is composed of a pin - up shoe , a die and a stiff back ...
... bending CRC - Evans PB12-16 and PB22-36 type bending machines were used for Pipes A and B , respectively . Figure 3 is an illustration of the bending machines . The bending machine is composed of a pin - up shoe , a die and a stiff back ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength