Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2002 - Arctic regions |
From inside the book
Results 1-3 of 53
Page 201
Organic coatings may electrically insulate the bolt from the structure , thereby insulating the coated bolt from the ... coating thickness may lead to inadequate bolting tolerances . For hot dip galvanised bolts oversized nuts will be ...
Organic coatings may electrically insulate the bolt from the structure , thereby insulating the coated bolt from the ... coating thickness may lead to inadequate bolting tolerances . For hot dip galvanised bolts oversized nuts will be ...
Page 301
... coating . The fatigue life of the coatings is found to be no longer than 103 cycles . None of the coatings resist above 103 cycles . It is found to be cracks initiation and propagation in the coating interface that result in the ...
... coating . The fatigue life of the coatings is found to be no longer than 103 cycles . None of the coatings resist above 103 cycles . It is found to be cracks initiation and propagation in the coating interface that result in the ...
Page 446
... coating depending on the laying method . Installation method Reeling S - lay J - lay Maximum strain on steel Maximum strain on coating 2 % 3 % 0.3 % 0.35 % 0.3 % 0.35 % In deeper waters in other areas of the world , the oxygen content ...
... coating depending on the laying method . Installation method Reeling S - lay J - lay Maximum strain on steel Maximum strain on coating 2 % 3 % 0.3 % 0.35 % 0.3 % 0.35 % In deeper waters in other areas of the world , the oxygen content ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength