Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2002 - Arctic regions |
From inside the book
Results 1-3 of 65
Page 311
... crack propagation phase and final failure unstable crack propagation . The first phase covers the crack initiation and the early crack growth state including cyclic plastic deformation prior to crack initiation of one or more macroscopic ...
... crack propagation phase and final failure unstable crack propagation . The first phase covers the crack initiation and the early crack growth state including cyclic plastic deformation prior to crack initiation of one or more macroscopic ...
Page 526
... crack growth measurements obtained from fatigue tests on full - scale girth welded pipes [ Maddox and Razmjoo , 1998 ] are used for such validation . Crack growth from known cracks at the toes of girth welds in pipes was predicted using ...
... crack growth measurements obtained from fatigue tests on full - scale girth welded pipes [ Maddox and Razmjoo , 1998 ] are used for such validation . Crack growth from known cracks at the toes of girth welds in pipes was predicted using ...
Page 527
... crack growth , both in the depth and length directions . It has to be borne in mind that these over - predictions were based on a C value that is below the mean value suggested in BS 7910 [ 2000 ] . By reviewing My solutions for welds ...
... crack growth , both in the depth and length directions . It has to be borne in mind that these over - predictions were based on a C value that is below the mean value suggested in BS 7910 [ 2000 ] . By reviewing My solutions for welds ...
Other editions - View all
Common terms and phrases
alloys analysis applied approximately assessment bending calculated carried coating compared composite compressive considered corrosion crack crack growth curve cycles damage defect deformation depth determined developed direction distribution effect element Engineering equation estimated evaluation experience factor failure fatigue field Figure flaw flexible fracture function geometry given Grade heat higher hydrogen important increase initial installation insulation integrity International joint length limit load locations lower material maximum mean measured mechanical method observed obtained Offshore operation parameters performed pipe plate predicted present pressure problem procedure production properties range reliability residual resistance respectively riser rope safety samples shown shows side simulation solution specimens standard steel strain strength stress structure surface Table temperature tensile tension thermal thickness titanium toughness uncertainties variables weld