... curve was proposed for the Heidrun drilling riser design , Thornton ( 1994 ) . This design curve has been superseded by a curve based on more recent data , as proposed by Baxter et al . ( 1997 ) , the Stolt - RMI design curve , N ( AS ) ...
... curve was proposed for the Heidrun drilling riser design , Thornton ( 1994 ) . This design curve has been superseded by a curve based on more recent data , as proposed by Baxter et al . ( 1997 ) , the Stolt - RMI design curve , N ( AS ) ...
Page 469
... curve could be taken as a design curve . However , due to limited sample size , these conclusions are uncertain . The data shown in Figure 4 may indicate that different design criteria ( SN curves ) may be needed for different weld ...
... curve could be taken as a design curve . However , due to limited sample size , these conclusions are uncertain . The data shown in Figure 4 may indicate that different design criteria ( SN curves ) may be needed for different weld ...
Page 476
... curves . The upper curve was proposed by Baxter et al . ( 1997 ) and is termed the Stolt - RMI curve : N ( AS ) 6 = 6.8-1019 ( 1 ) The lower curve is proposed herein , and is termed the MARINTEK curve , N ( AS ) 5 = 9.6.1016 ( 2 ) ...
... curves . The upper curve was proposed by Baxter et al . ( 1997 ) and is termed the Stolt - RMI curve : N ( AS ) 6 = 6.8-1019 ( 1 ) The lower curve is proposed herein , and is termed the MARINTEK curve , N ( AS ) 5 = 9.6.1016 ( 2 ) ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength