... important ageing phenomenon in PA11 . The process is well understood due to intense recent research . The kinetics of molecular weight loss are known in detail and can rather well be correlated with material performance [ 5 , 6 , 7 , 8 ] ...
... important ageing phenomenon in PA11 . The process is well understood due to intense recent research . The kinetics of molecular weight loss are known in detail and can rather well be correlated with material performance [ 5 , 6 , 7 , 8 ] ...
Page 462
purpose , however it is important to understand that the fatigue frequency is an important issue for coatings , not in terms of fatigue life , but for heat generation . High frequency testing is convenient as the test is completed ...
purpose , however it is important to understand that the fatigue frequency is an important issue for coatings , not in terms of fatigue life , but for heat generation . High frequency testing is convenient as the test is completed ...
Page 552
... important in assessing the capacity of a structure containing damage , e.g. a large fatigue crack . Existing codes and standards are based on satisfying component adequacy and hence structures are normally designed on a component basis ...
... important in assessing the capacity of a structure containing damage , e.g. a large fatigue crack . Existing codes and standards are based on satisfying component adequacy and hence structures are normally designed on a component basis ...
Other editions - View all
Common terms and phrases
alloys analysis applied approximately assessment bending calculated carried coating compared composite compressive considered corrosion crack crack growth curve cycles damage defect deformation depth determined developed direction distribution effect element Engineering equation estimated evaluation experience factor failure fatigue field Figure flaw flexible fracture function geometry given Grade heat higher hydrogen important increase initial installation insulation integrity International joint length limit load locations lower material maximum mean measured mechanical method observed obtained Offshore operation parameters performed pipe plate predicted present pressure problem procedure production properties range reliability residual resistance respectively riser rope safety samples shown shows side simulation solution specimens standard steel strain strength stress structure surface Table temperature tensile tension thermal thickness titanium toughness uncertainties variables weld