21st International Conference on Offshore Mechanics EVALUATION OF WELDING RESIDUAL STRESSES IN POWER PLANT ... stress is one of the important problems in welding design / fabrications and sound maintenance of welded structures . Thus ...
21st International Conference on Offshore Mechanics EVALUATION OF WELDING RESIDUAL STRESSES IN POWER PLANT ... stress is one of the important problems in welding design / fabrications and sound maintenance of welded structures . Thus ...
Page 250
... residual stresses in weldment including heat- affected zones ( HAZs ) ... residual stresses in weldment in this study . Many studies have been conducted on ... stress state Lo LT Stress free state Tensile 250 Copyright © 2002 by ASME.
... residual stresses in weldment including heat- affected zones ( HAZs ) ... residual stresses in weldment in this study . Many studies have been conducted on ... stress state Lo LT Stress free state Tensile 250 Copyright © 2002 by ASME.
Page 253
... residual stress ( σ , in Fig . 5 ) by saw - cutting technique , strain gages were attached along the distance from weld centerline . The gages were providing information about relaxed residual stress value during cutting . Signals from ...
... residual stress ( σ , in Fig . 5 ) by saw - cutting technique , strain gages were attached along the distance from weld centerline . The gages were providing information about relaxed residual stress value during cutting . Signals from ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength