... shows the schematic illustration of the partial gas burst test apparatus . The test pipes were placed on a bed of straw bales with the machined notch facing upwards . The test pipes were partially filled to 85 % with a mixture of brine ...
... shows the schematic illustration of the partial gas burst test apparatus . The test pipes were placed on a bed of straw bales with the machined notch facing upwards . The test pipes were partially filled to 85 % with a mixture of brine ...
Page 227
... show the same value . From the measurement of strains shown in Figs.4 , 5 and 6 , the strain at 80mm remote from the center was employed as the reference strain in subsequent discussion . Strain Figure 7 shows the comparison of nominal ...
... show the same value . From the measurement of strains shown in Figs.4 , 5 and 6 , the strain at 80mm remote from the center was employed as the reference strain in subsequent discussion . Strain Figure 7 shows the comparison of nominal ...
Page 230
... shows higher value than Steel B at the flaw front . In addition , the strain distribution in Steel C around the flaw front shows wider extension of high plastic strain area compared with that of Steel B. The differences in the maximum ...
... shows higher value than Steel B at the flaw front . In addition , the strain distribution in Steel C around the flaw front shows wider extension of high plastic strain area compared with that of Steel B. The differences in the maximum ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength