Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2002 - Arctic regions |
From inside the book
Results 1-3 of 97
Page 150
... tensile residual stress ( tensile hydrostatic stress ) is occurred at the crack initiation point after unloading , and tensile stress increase in the process of loading . unloading . It is able to be supposed that large tensile stress ...
... tensile residual stress ( tensile hydrostatic stress ) is occurred at the crack initiation point after unloading , and tensile stress increase in the process of loading . unloading . It is able to be supposed that large tensile stress ...
Page 189
... TENSILE PROPERTIES DUE TO COLD BENDING OF LINE PIPES Hiroshi YATABE Tomoki MASUDA Pipeline Engineering Research Laboratory , Tokyo Gas Co. , Ltd. , 1-7-7 , Suehiro - cho , Tsurumi - ku , Yokohama , 230-0045 , JAPAN Bending location Pin ...
... TENSILE PROPERTIES DUE TO COLD BENDING OF LINE PIPES Hiroshi YATABE Tomoki MASUDA Pipeline Engineering Research Laboratory , Tokyo Gas Co. , Ltd. , 1-7-7 , Suehiro - cho , Tsurumi - ku , Yokohama , 230-0045 , JAPAN Bending location Pin ...
Page 190
... tensile specimens were machined from the pipes in the longitudinal direction . Figure 1 illustrates the tensile specimen with a thickness of 12 mm . Figure 2 shows the stress - strain relationship of the pipes . Pipe B had a yield ...
... tensile specimens were machined from the pipes in the longitudinal direction . Figure 1 illustrates the tensile specimen with a thickness of 12 mm . Figure 2 shows the stress - strain relationship of the pipes . Pipe B had a yield ...
Other editions - View all
Common terms and phrases
alloys analysis applied approximately assessment bending calculated carried coating compared composite compressive considered corrosion crack crack growth curve cycles damage defect deformation depth determined developed direction distribution effect element Engineering equation estimated evaluation experience factor failure fatigue field Figure flaw flexible fracture function geometry given Grade heat higher hydrogen important increase initial installation insulation integrity International joint length limit load locations lower material maximum mean measured mechanical method observed obtained Offshore operation parameters performed pipe plate predicted present pressure problem procedure production properties range reliability residual resistance respectively riser rope safety samples shown shows side simulation solution specimens standard steel strain strength stress structure surface Table temperature tensile tension thermal thickness titanium toughness uncertainties variables weld