Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2002 - Arctic regions |
From inside the book
Results 1-3 of 82
Page 333
... welding conditions for the different test welds are given : Number of demonstration weld ( s ) Dimensions Welding method Welding Welding position Heat Treatment Non Destructive Testing ( NDT ) Aker Offshore Partner 1 , designated AOP in ...
... welding conditions for the different test welds are given : Number of demonstration weld ( s ) Dimensions Welding method Welding Welding position Heat Treatment Non Destructive Testing ( NDT ) Aker Offshore Partner 1 , designated AOP in ...
Page 518
... welding procedures , which provided a range of weld penetrations at different travel speeds . 2.1.3 Discrete Dual Process Welded Joints The laser and arc welding trials provided data that enabled the dual process welds to be carried out ...
... welding procedures , which provided a range of weld penetrations at different travel speeds . 2.1.3 Discrete Dual Process Welded Joints The laser and arc welding trials provided data that enabled the dual process welds to be carried out ...
Page 524
... welding technologies to weld steel plate . The following conclusions were deduced : Stage 1 : Discrete arc and laser welding : Satisfactory arc and laser welds have been produced in the same joint . The welds produced for this work ...
... welding technologies to weld steel plate . The following conclusions were deduced : Stage 1 : Discrete arc and laser welding : Satisfactory arc and laser welds have been produced in the same joint . The welds produced for this work ...
Other editions - View all
Common terms and phrases
21st International Conference alloys analysis anchor applied assessment axial calculated coating coefficient composite compressive Conference on Offshore corrosion crack growth crack initiation damage defect deformation depth Det Norske Veritas developed diameter displacement distribution effect Engineering June 23-28 equation evaluation failure fatigue crack fatigue test Figure finite element flaw flexible pipe flowline fracture mechanics fracture toughness function Grade heat hydrogen hydrogen embrittlement ice load increase installation insulation integrity joint laser weld layer length longitudinal maximum measured mechanical properties method Norsk Hydro Norway Offshore Mechanics parameters performed piezoelectric pipeline plastic plate predicted pressure reliability residual stress rope S-N curve safety factors sensors shown simulation solution specimens steel strain strength stress range surface syntactic foam Table Technology temperature tensile tension thermal thermal conductivity thermal insulation thickness titanium titanium risers uncertainties variables velocity Weibull distribution yield strength