Low-dielectric Constant Materials, Volume 476Materials Research Society, 1997 - Electric insulators and insulation |
From inside the book
Results 1-3 of 30
Page 19
... resistance to oxygen plasma . This study describes adhesion failure mechanisms for the sandwiched fluorinated amorphous carbon film ( a - C : F ) structure during oxygen plasma annealing . We have found 3 failure modes : 1 ) capping ...
... resistance to oxygen plasma . This study describes adhesion failure mechanisms for the sandwiched fluorinated amorphous carbon film ( a - C : F ) structure during oxygen plasma annealing . We have found 3 failure modes : 1 ) capping ...
Page 20
... resistance . EXPERIMENTAL 4 The low - k multidielectric ILD was deposited on aluminum metal lines ( metal 1 ) at a ... resistance of the oxygen plasma process depends on the depth of silicon oxide , even if the oxygen plasma resistance ...
... resistance . EXPERIMENTAL 4 The low - k multidielectric ILD was deposited on aluminum metal lines ( metal 1 ) at a ... resistance of the oxygen plasma process depends on the depth of silicon oxide , even if the oxygen plasma resistance ...
Page 121
... resistance , higher T , and low dielectric constant are properties that make this e - beam cured poly ( arylene ether ) film an excellent candidate for interlevel dielectric integration processes . g g TM INTRODUCTION As integrated ...
... resistance , higher T , and low dielectric constant are properties that make this e - beam cured poly ( arylene ether ) film an excellent candidate for interlevel dielectric integration processes . g g TM INTRODUCTION As integrated ...
Contents
Polynorbornene for Lowk Interconnection | 3 |
SILK Polymer Coating With LowDielectric Constant | 9 |
F During Oxygen Plasma Annealing | 19 |
Copyright | |
34 other sections not shown
Other editions - View all
Common terms and phrases
adhesion aerogel annealing as-deposited atoms BCB film bond BPDA-PDA capacitance Chemat-B chemical cm¹ CMP process coating copolymers cured films curve decrease delamination density deposition rate device dielectric constant dielectric material diffusion e-beam cured effect electron Figure film stress film thickness films deposited fluorinated polyimide fluorine fluoropolymer FSG films FTEOS films FTIR gap fill glass transition temperature heating in-plane increase integrated circuits interface labile block layer low dielectric constant low-k measured mechanical metal lines modulus moisture Multilevel Interconnection norbornene optical out-of-plane oxide oxygen PA-N film parylene Parylene-N peak PECVD Phys planarization plasma plasma treatment polishing polyimide polymer polymerization precursor pressure Proc properties PTFE ratio reaction refractive index sample shows Si-F Si-O-Si silica silicon SiO2 SiOF films slurry spectra spin-coated spin-on structure substrate surface Teflon-AF temperature TEOS thermal cycles thermal stability thin films ULSI vapor wafer wet etch