Deformation and Fracture Mechanics of Engineering MaterialsUpdated to reflect recent developments in our understanding of deformation and fracture processes in structural materials. This completely revised reference includes new sections on isostress analysis, modulus of rupture, creep fracture micromechanicsms, and many more. |
From inside the book
Results 1-3 of 84
Page 131
... associated with a screw dislocation , whereas both shear and hydrostatic stress fields surround an edge dislo- cation . Regarding the latter , one finds that the edge dislocation is surrounded by combined shear / hydrostatic stress ...
... associated with a screw dislocation , whereas both shear and hydrostatic stress fields surround an edge dislo- cation . Regarding the latter , one finds that the edge dislocation is surrounded by combined shear / hydrostatic stress ...
Page 487
... associated with these processes . For convenience of this discussion , these phenomena are referred to collectively as envi- ronment - assisted cracking ( EAC ) . Indeed , Ford " has referred to such classifications of SCC , HE , LME ...
... associated with these processes . For convenience of this discussion , these phenomena are referred to collectively as envi- ronment - assisted cracking ( EAC ) . Indeed , Ford " has referred to such classifications of SCC , HE , LME ...
Page 743
... associated with the fatigue fracture of HiPS was found to be approximately 2.4 MPam in good agreement with the estimated Kmax of 2.2 MPa / m for the toilet seat . Finally , the last few fatigue bands seen on the fracture surface were ...
... associated with the fatigue fracture of HiPS was found to be approximately 2.4 MPam in good agreement with the estimated Kmax of 2.2 MPa / m for the toilet seat . Finally , the last few fatigue bands seen on the fracture surface were ...
Other editions - View all
Common terms and phrases
addition alloy aluminum alloy applied stress associated ASTM atoms behavior brittle ceramics Chapter Charpy component composite crack extension crack growth crack length crack tip craze creep rate crystal curve cyclic decrease depends determined dislocation ductility elastic embrittlement engineering example factor failure fiber FIGURE flaw fracture mechanics fracture surface fracture toughness given grain boundaries hardening hydrogen increasing initial KIEAC lattice load maraging steels martensite material material's matrix Metals Park microstructure microvoid modulus notch Note occur oriented parameter particles phase plane plane-strain plastic deformation plastic zone plate polymer polymeric region relative Reprinted with permission result rupture sample screw dislocation Section shear stress shown in Fig solid solution specimen stacking fault energy steel alloys strain rate stress concentration stress field stress intensity stress level stress-strain stress-strain curve superalloys tensile stress test temperature thermal thickness toughening Trans transition temperature twinning values yield strength