The system and technique are those described above . To determine the ester
interchange reaction rate , the authors annealed the films at 200 and 225°C .
Table 4 shows the duration of annealing and how many DEG units were
transferred .
The system and technique are those described above . To determine the ester
interchange reaction rate , the authors annealed the films at 200 and 225°C .
Table 4 shows the duration of annealing and how many DEG units were
transferred .
Page 23
30 , 000 ) , were mixed in a common solvent ; voidfree films were prepared
thereafter and annealed at different ... The result indicates that ester - exchange
reactions between protonated and deuterated PET require higher annealing ...
30 , 000 ) , were mixed in a common solvent ; voidfree films were prepared
thereafter and annealed at different ... The result indicates that ester - exchange
reactions between protonated and deuterated PET require higher annealing ...
Page 92
But after annealing at temperatures below the glass transition an endothermic
peak develops as temperature is scanned through the glass transition [ 70 , 71 ) .
The height of this peak increases with the duration of the sub - T , annealing .
But after annealing at temperatures below the glass transition an endothermic
peak develops as temperature is scanned through the glass transition [ 70 , 71 ) .
The height of this peak increases with the duration of the sub - T , annealing .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Common terms and phrases
achieved acid additional amorphous annealing Appl applied aspect average behavior block bonding changes Chem chemical composites conclusion constant crack crystallinity crystallization curves decreases deformation density depends determined diameter diffusion direction distribution domains draw ratio drawn effect element energy Equation experiments extrusion factor fatigue fiber Figure fracture fracture toughness function given groups growth healing heat higher important increasing indicated initial length linear load lower material matrix maximum measurements mechanical melt method microfibrils microstructure modulus molded molecular weight molecules nylon nylon 66 observed obtained occurs orientation peak phase Phys polyamides polycondensation polyesters Polymer Sci polymerization properties range reaction regions reported Reprinted from Ref respectively samples SAXS scattering shows solid solid state polycondensation solid-state specimen speed stage strain strength stress structure studied Table temperature tensile units values yield
Bibliographic information
| Title | Solid State Behavior of Linear Polyesters and Polyamides Prentice Hall International Series in the Physical and Chemi Prentice-Hall international series in the physical and chemical engineering sciences |
| Authors | Jerold M. Schultz, Stoyko Fakirov |
| Editors | Jerold M. Schultz, Stoyko Fakirov |
| Edition | illustrated |
| Publisher | Prentice Hall, 1990 |
| Original from | the University of Michigan |
| Digitized | 15 Dec 2007 |
| ISBN | 0138247315, 9780138247317 |
| Length | 325 pages |
| Subjects | › Technology & Engineering / General |
| Export Citation | BiBTeX EndNote RefMan |