Solid state behavior of linear polyesters and polyamides |
From inside the book
Results 1-3 of 28
Page 121
Crystallization during spinning is associated with the formation of a neck in the
threadline [158,159,167]. George et al. [159] show that the region of rapid
diameter change along the threadline becomes increasingly localized with
increasing ...
Crystallization during spinning is associated with the formation of a neck in the
threadline [158,159,167]. George et al. [159] show that the region of rapid
diameter change along the threadline becomes increasingly localized with
increasing ...
Page 185
measurements were made of the filament temperature and diameter at each
sleeve. The filament temperature was also measured by the contact null-point
device, and the filament diameter was measured by close-up photography. Thus,
by ...
measurements were made of the filament temperature and diameter at each
sleeve. The filament temperature was also measured by the contact null-point
device, and the filament diameter was measured by close-up photography. Thus,
by ...
Page 191
Filament diameter measurement. Reprinted from Ref. [52] by courtesy of The
Society of Plastic Engineers. and, at a given point, a fiber of almost uniform cross
section is obtained (Type II). (The local draw ratio is determined by comparing the
...
Filament diameter measurement. Reprinted from Ref. [52] by courtesy of The
Society of Plastic Engineers. and, at a given point, a fiber of almost uniform cross
section is obtained (Type II). (The local draw ratio is determined by comparing the
...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
SUMMARY | 1 |
TRANSREACTIONS AND POSTADDITIONAL | 19 |
CHEMICAL HEALING | 43 |
Copyright | |
18 other sections not shown
Common terms and phrases
acid additional solid amorphous annealing Appl aspect ratio behavior birefringence block temperature chain Chem composites condensation copolyester copolymer courtesy crystallinity crystallization curves decrease deformation degree of crystallinity density diameter diffusion domains draw ratio Droscher effect Equation exchange reactions extrusion temperature Fakirov fiber axis fibers drawn filament fracture mechanics fracture toughness function heated element higher increase initial kinetics linear polycondensates load macromolecules Makromol material matrix maximum measurements mechanical melting point microfibrils microstructure modulus molded molecules morphology Nelon nominal draw ratio noncrystalline nylon 6 fibers nylon 66 obtained orientation parameters peak PET fibers phase Phys Plastic poly polyamides polyesters Polymer Sci polymerization properties Reprinted from Ref samples SAXS Schultz semicrystalline shown in Figure solid state polycondensation solid state post-polycondensation solid state reactions Solid-state extrusion specimen spherulite spinning strength stress structure Table tensile terephthalate thermoplastics toughened transesterification transreactions values x-ray yield Zachmann
Bibliographic information
| Title | Solid state behavior of linear polyesters and polyamides Prentice Hall international series in the physical and chemical engineering sciences Prentice Hall International Series in the Physical and Chemi |
| Authors | Jerold M. Schultz, Stoĭko Fakirov |
| Editors | Jerold M. Schultz, Stoĭko Fakirov |
| Contributor | Jerold M. Schultz |
| Edition | illustrated |
| Publisher | Prentice Hall, 1990 |
| Original from | the University of Michigan |
| Digitized | 15 Dec 2007 |
| ISBN | 0138247315, 9780138247317 |
| Length | 325 pages |
| Subjects | › › Polyesters Polyimides Science / Chemistry / Inorganic Technology & Engineering / Chemical & Biochemical Technology & Engineering / Material Science Technology & Engineering / Textiles & Polymers |
| Export Citation | BiBTeX EndNote RefMan |