Solid State Behavior of Linear Polyesters and Polyamides |
From inside the book
Results 1-3 of 61
Page 56
... experiments with crosslinked polyamides and the results obtained may be considered as an indication of the existence of chemically released diffusion in the solid statemotion of chain segments caused by inter- and intrachain chemical ...
... experiments with crosslinked polyamides and the results obtained may be considered as an indication of the existence of chemically released diffusion in the solid statemotion of chain segments caused by inter- and intrachain chemical ...
Page 98
... EXPERIMENTS A. IN SITU TEMPERATURE 1 2 3 4 5 MEASUREMENTS TIME B. TREAT AND QUENCH ( TAQ ) TEMPERATURE 3 SPECIMENS TIME Figure 12. Types of kinetic experiments : ( a ) treat and quench ( TRAQ ) experiments , in which glassy specimens ...
... EXPERIMENTS A. IN SITU TEMPERATURE 1 2 3 4 5 MEASUREMENTS TIME B. TREAT AND QUENCH ( TAQ ) TEMPERATURE 3 SPECIMENS TIME Figure 12. Types of kinetic experiments : ( a ) treat and quench ( TRAQ ) experiments , in which glassy specimens ...
Page 229
... experiments with this type of material was carried out under ram conditions by Dröscher and Regel [ 26 ] . Applying a rectan- gular die , they obtained a well - oriented sample at 190 ° C , which was about 22 ° K below the melting ...
... experiments with this type of material was carried out under ram conditions by Dröscher and Regel [ 26 ] . Applying a rectan- gular die , they obtained a well - oriented sample at 190 ° C , which was about 22 ° K below the melting ...
Contents
SOLID STATE REACTIONS IN LINEAR | 1 |
CHEMICAL HEALING | 43 |
PRACTICAL ASPECTS OF ADDITIONAL SOLID STATE | 59 |
Copyright | |
19 other sections not shown
Common terms and phrases
acid additional solid amorphous annealing Appl aspect ratio behavior birefringence block temperature chain Chem composites copolyester copolymer courtesy crystallinity crystallization curves decreases deformation degree of crystallinity density diameter diffusion domains Dröscher effect Equation exchange reactions extrusion temperature Fakirov fiber axis fibers drawn filament fracture mechanics fracture toughness function heat of fusion heated element higher increasing initial kg/cm² kinetics linear polycondensates load macromolecules Makromol material matrix maximum measurements mechanical melting point microfibrils microstructure mm/min modulus molded molecules morphology nominal draw ratio noncrystalline nylon 6 fibers nylon 66 orientation parameters peak PET fibers phase Phys polyamides polyesters Polymer Sci polymerization properties Reprinted from Ref samples SAXS Schultz semicrystalline shown in Figure solid state polycondensation solid state post-polycondensation solid state reactions Solid-state extrusion specimen spherulite strength stress structure Table tensile terephthalate thermoplastics toughened transesterification transreactions values x-ray yield Zachmann