Page 79
Structure of Melts and Glasses The processing of polyesters and polyamides ... In
order to understand the structure ( and properties ) of the final state , it is useful
first to understand the structure of the melt or glass which is its precursor .
Structure of Melts and Glasses The processing of polyesters and polyamides ... In
order to understand the structure ( and properties ) of the final state , it is useful
first to understand the structure of the melt or glass which is its precursor .
Page 110
Such fibers have been subjected to molecular orientation and heat - treatment
during processing . While it is difficult to observe fine structure on the surface of
PET fibers ( 124 ) , a fibrillar fine structure is observed once the outer skin of the
fiber ...
Such fibers have been subjected to molecular orientation and heat - treatment
during processing . While it is difficult to observe fine structure on the surface of
PET fibers ( 124 ) , a fibrillar fine structure is observed once the outer skin of the
fiber ...
Page 134
ially oriented polymer structures suggest that microfibrils are essential and
probably unavoidable products of the conversion ... In the microfibrilar structure ,
the crystallite length along the microfibril aris is always about 2 , 3 of the loag
period .
ially oriented polymer structures suggest that microfibrils are essential and
probably unavoidable products of the conversion ... In the microfibrilar structure ,
the crystallite length along the microfibril aris is always about 2 , 3 of the loag
period .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Common terms and phrases
achieved acid additional amorphous annealing Appl applied aspect average behavior block bonding changes Chem chemical composites conclusion constant crack crystallinity crystallization curves decreases deformation density depends determined diameter diffusion direction distribution domains draw ratio drawn effect element energy Equation experiments extrusion factor fatigue fiber Figure fracture fracture toughness function given groups growth healing heat higher important increasing indicated initial length linear load lower material matrix maximum measurements mechanical melt method microfibrils microstructure modulus molded molecular weight molecules nylon nylon 66 observed obtained occurs orientation peak phase Phys polyamides polycondensation polyesters Polymer Sci polymerization properties range reaction regions reported Reprinted from Ref respectively samples SAXS scattering shows solid solid state polycondensation solid-state specimen speed stage strain strength stress structure studied Table temperature tensile units values yield