MODULUS Tensile and bending moduli are very important textile properties [
2729 ) . Although the bending modulus appears in many equations describing
the behavior of fabrics and other textile structures , it is seldom determined in
textile ...
MODULUS Tensile and bending moduli are very important textile properties [
2729 ) . Although the bending modulus appears in many equations describing
the behavior of fabrics and other textile structures , it is seldom determined in
textile ...
Page 187
( 51 ] by courtesy of John Wiley and Sons , Inc . maximum tensile strength of the
drawn yarn were established by experiments , and the real - time history of
temperature and elongational rates were compared ( see Figure 31 ) .
( 51 ] by courtesy of John Wiley and Sons , Inc . maximum tensile strength of the
drawn yarn were established by experiments , and the real - time history of
temperature and elongational rates were compared ( see Figure 31 ) .
Page 216
33 10 - 4 5 - 1 using an Instron tensile testing machine model TTCM , equipped
with a 10 mm strain extensometer . The tensile modulus , as well as the
crystallinity , increased with Rp for melt - crystallized PA 6 ( Figure 3 ) . The
highest draw ...
33 10 - 4 5 - 1 using an Instron tensile testing machine model TTCM , equipped
with a 10 mm strain extensometer . The tensile modulus , as well as the
crystallinity , increased with Rp for melt - crystallized PA 6 ( Figure 3 ) . The
highest draw ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Common terms and phrases
achieved acid additional amorphous annealing Appl applied aspect average behavior block bonding changes Chem chemical composites conclusion constant crack crystallinity crystallization curves decreases deformation density depends determined diameter diffusion direction distribution domains draw ratio drawn effect element energy Equation experiments extrusion factor fatigue fiber Figure fracture fracture toughness function given groups growth healing heat higher important increasing indicated initial length linear load lower material matrix maximum measurements mechanical melt method microfibrils microstructure modulus molded molecular weight molecules nylon nylon 66 observed obtained occurs orientation peak phase Phys polyamides polycondensation polyesters Polymer Sci polymerization properties range reaction regions reported Reprinted from Ref respectively samples SAXS scattering shows solid solid state polycondensation solid-state specimen speed stage strain strength stress structure studied Table temperature tensile units values yield
Bibliographic information
| Title | Solid State Behavior of Linear Polyesters and Polyamides Prentice Hall International Series in the Physical and Chemi Prentice-Hall international series in the physical and chemical engineering sciences |
| Authors | Jerold M. Schultz, Stoyko Fakirov |
| Editors | Jerold M. Schultz, Stoyko Fakirov |
| Edition | illustrated |
| Publisher | Prentice Hall, 1990 |
| Original from | the University of Michigan |
| Digitized | 15 Dec 2007 |
| ISBN | 0138247315, 9780138247317 |
| Length | 325 pages |
| Subjects | › Technology & Engineering / General |
| Export Citation | BiBTeX EndNote RefMan |