Solid State Behavior of Linear Polyesters and Polyamides |
From inside the book
Results 1-3 of 12
Page 264
... toughened PA - 6.6 [ 66 , 84 ] . It was also demonstrated that Jie increases with increasing crystallinity for material of identical composition [ 66 ] . The ef- fect of impact - modifier content on fracture toughness at different ...
... toughened PA - 6.6 [ 66 , 84 ] . It was also demonstrated that Jie increases with increasing crystallinity for material of identical composition [ 66 ] . The ef- fect of impact - modifier content on fracture toughness at different ...
Page 265
... toughened PA - 6 in function of tempera- ture ( T ) , crosshead speed ( v ) and impact modifier content . Designation : more toughened resin Durethan BC 303 , less toughened resin = Durethan BC 402 ; ( cf. also Figure 13 ) . 4 6 8 10 ...
... toughened PA - 6 in function of tempera- ture ( T ) , crosshead speed ( v ) and impact modifier content . Designation : more toughened resin Durethan BC 303 , less toughened resin = Durethan BC 402 ; ( cf. also Figure 13 ) . 4 6 8 10 ...
Page 292
... toughened 0.00017 Hz | દ No GC.M ( tough ) > 30 Gc , c = 5-30 Gc decreases with increasing vf .KQ slightly increases with increasing VF for the rubber toughened grade ( KQ , c = 12-16 MPam1 / 2 ) , however it goes through a minimum in ...
... toughened 0.00017 Hz | દ No GC.M ( tough ) > 30 Gc , c = 5-30 Gc decreases with increasing vf .KQ slightly increases with increasing VF for the rubber toughened grade ( KQ , c = 12-16 MPam1 / 2 ) , however it goes through a minimum in ...
Contents
SOLID STATE REACTIONS IN LINEAR | 1 |
CHEMICAL HEALING | 43 |
PRACTICAL ASPECTS OF ADDITIONAL SOLID STATE | 59 |
Copyright | |
19 other sections not shown
Common terms and phrases
acid additional solid amorphous annealing Appl aspect ratio behavior birefringence block temperature chain Chem composites copolyester copolymer courtesy crystallinity crystallization curves decreases deformation degree of crystallinity density diameter diffusion domains Dröscher effect Equation exchange reactions extrusion temperature Fakirov fiber axis fibers drawn filament fracture mechanics fracture toughness function heat of fusion heated element higher increasing initial kg/cm² kinetics linear polycondensates load macromolecules Makromol material matrix maximum measurements mechanical melting point microfibrils microstructure mm/min modulus molded molecules morphology nominal draw ratio noncrystalline nylon 6 fibers nylon 66 orientation parameters peak PET fibers phase Phys polyamides polyesters Polymer Sci polymerization properties Reprinted from Ref samples SAXS Schultz semicrystalline shown in Figure solid state polycondensation solid state post-polycondensation solid state reactions Solid-state extrusion specimen spherulite strength stress structure Table tensile terephthalate thermoplastics toughened transesterification transreactions values x-ray yield Zachmann