Page 277
... CGHAZ . The specimen for SCR CGHAZ showed the highest value . Especially , the values of the synthetic IC CGHAZ for both SMAW and SAW were lower than required minimum impact value of improved 9 % Ni steel at 77K , 35 J , in the several ...
... CGHAZ . The specimen for SCR CGHAZ showed the highest value . Especially , the values of the synthetic IC CGHAZ for both SMAW and SAW were lower than required minimum impact value of improved 9 % Ni steel at 77K , 35 J , in the several ...
Page 278
... CGHAZ and SCR CGHAZ exhibited the similar behaviors with synthetic IC CGHAZ specimen not sub - zero treated , i.e. ductile fracture with heavy deformation occurred without any brittle fracture . Figure 10 shows the examples of the load ...
... CGHAZ and SCR CGHAZ exhibited the similar behaviors with synthetic IC CGHAZ specimen not sub - zero treated , i.e. ductile fracture with heavy deformation occurred without any brittle fracture . Figure 10 shows the examples of the load ...
Page 279
... CGHAZ . Therefore the IC CGHAZ only at cryogenic temperature was called " cryogenic LBZ ” in this study . ( 2 ) It was found that retained austenite was not an effective factor . So , M - A were focused as another metallurgical factor ...
... CGHAZ . Therefore the IC CGHAZ only at cryogenic temperature was called " cryogenic LBZ ” in this study . ( 2 ) It was found that retained austenite was not an effective factor . So , M - A were focused as another metallurgical factor ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength