... CGHAZ . The specimen for SCR CGHAZ showed the highest value . Especially , the values of the synthetic IC CGHAZ for both SMAW and SAW were lower than required minimum impact value of improved 9 % Ni steel at 77K , 35 J , in the several ...
... CGHAZ . The specimen for SCR CGHAZ showed the highest value . Especially , the values of the synthetic IC CGHAZ for both SMAW and SAW were lower than required minimum impact value of improved 9 % Ni steel at 77K , 35 J , in the several ...
Page 278
... CGHAZ and SCR CGHAZ exhibited the similar behaviors with synthetic IC CGHAZ specimen not sub - zero treated , i.e. ductile fracture with heavy deformation occurred without any brittle fracture . Figure 10 shows the examples of the load ...
... CGHAZ and SCR CGHAZ exhibited the similar behaviors with synthetic IC CGHAZ specimen not sub - zero treated , i.e. ductile fracture with heavy deformation occurred without any brittle fracture . Figure 10 shows the examples of the load ...
Page 279
... CGHAZ . Therefore the IC CGHAZ only at cryogenic temperature was called " cryogenic LBZ ” in this study . ( 2 ) It was found that retained austenite was not an effective factor . So , M - A were focused as another metallurgical factor ...
... CGHAZ . Therefore the IC CGHAZ only at cryogenic temperature was called " cryogenic LBZ ” in this study . ( 2 ) It was found that retained austenite was not an effective factor . So , M - A were focused as another metallurgical factor ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield