Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 34
Page 56
... CTOD values were directly measured across the fatigue crack tip ( 5mm gauge length ) on both sides of the SENB specimens . The CTOD 8 , method developed at GKSS Research Centre , provides intrinsic toughness values based on local ...
... CTOD values were directly measured across the fatigue crack tip ( 5mm gauge length ) on both sides of the SENB specimens . The CTOD 8 , method developed at GKSS Research Centre , provides intrinsic toughness values based on local ...
Page 255
... CTOD value requirement at -10 ° C , to secure adequate fracture toughness . Particularly , the structures for Sakhalin region requires not only YS 420 MPa , but also extremely strict nil - ductility transition lower than -85 ° C and CTOD ...
... CTOD value requirement at -10 ° C , to secure adequate fracture toughness . Particularly , the structures for Sakhalin region requires not only YS 420 MPa , but also extremely strict nil - ductility transition lower than -85 ° C and CTOD ...
Page 267
... CTOD ( mm ) ( b ) Matched joint 2 3.0 0.02 0.05 0.1 888 ם ום m m 0.5 1.0 Critical CTOD ( mm ) ( c ) Undermatched joint Fig . 6 Distributions of critical CTOD values ... CTOD concept . Table 2 Weibull parameters for X80 steel welds . Critical ...
... CTOD ( mm ) ( b ) Matched joint 2 3.0 0.02 0.05 0.1 888 ם ום m m 0.5 1.0 Critical CTOD ( mm ) ( c ) Undermatched joint Fig . 6 Distributions of critical CTOD values ... CTOD concept . Table 2 Weibull parameters for X80 steel welds . Critical ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength