... Table 11 Results of Y - joints under axial loading 2.38 2.45 6.72 0.64 5.66 6.06 2.99 0.51 2.49 2.45 3.30 0.42 1.86 2.58 3.39 2.95 2.83 5.89 0.59 5.04 6.23 T3 T4 7.24 10.27 4.41 1.28 9.97 0.70 10.09 11.16 Joint Current Efthymiou 6.66 ...
... Table 11 Results of Y - joints under axial loading 2.38 2.45 6.72 0.64 5.66 6.06 2.99 0.51 2.49 2.45 3.30 0.42 1.86 2.58 3.39 2.95 2.83 5.89 0.59 5.04 6.23 T3 T4 7.24 10.27 4.41 1.28 9.97 0.70 10.09 11.16 Joint Current Efthymiou 6.66 ...
Page 250
Table 2 Chemical composition of the X80 steel produced . C Si Mn P S ΑΙ TI Nb N 0.05 0.11 1.8 0.01 0.002 0.03 0.01 0.05 0.003 Pcm = C + Si / 30 + ( Mn + Cu + Cr ) / 20 + Mo / 15 + V / 10 + Ni / 60 + B Table 6 Welding conditions of girth ...
Table 2 Chemical composition of the X80 steel produced . C Si Mn P S ΑΙ TI Nb N 0.05 0.11 1.8 0.01 0.002 0.03 0.01 0.05 0.003 Pcm = C + Si / 30 + ( Mn + Cu + Cr ) / 20 + Mo / 15 + V / 10 + Ni / 60 + B Table 6 Welding conditions of girth ...
Page 259
Table 4 Mechanical properties of base metal Table 5 Effect of strain aging on Charpy impact properties Strain and Charpy impact properties Location Direction aging " Absorbed energy ( J ) 50 % -60 ° C -80 ° C -100 °C | FATT ( C ) -10-20 ...
Table 4 Mechanical properties of base metal Table 5 Effect of strain aging on Charpy impact properties Strain and Charpy impact properties Location Direction aging " Absorbed energy ( J ) 50 % -60 ° C -80 ° C -100 °C | FATT ( C ) -10-20 ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield