However , the SEM analysis of tested specimens has indicated significant
differences in fracture surface roughness , crack front profiles and fracture modes
in the base material and HAZ / CR ( Figure 5 - Figure 7 ) . At the HAZ and CR the
...
However , the SEM analysis of tested specimens has indicated significant
differences in fracture surface roughness , crack front profiles and fracture modes
in the base material and HAZ / CR ( Figure 5 - Figure 7 ) . At the HAZ and CR the
...
Page 148
The gauge areas of the SN - specimens covered both , base material as well as
consumable ring ( CR ) . The fatigue tests have been performed under load
control ( sinusoidal wave form ) with a frequency of 0 . 2 Hz ( representing wave ...
The gauge areas of the SN - specimens covered both , base material as well as
consumable ring ( CR ) . The fatigue tests have been performed under load
control ( sinusoidal wave form ) with a frequency of 0 . 2 Hz ( representing wave ...
Page 150
Table 2 : Tensile tests on round specimens , axial test direction ( all base material
, Ø = 3 mm ) . Test temperature Roo . 2 Rm A5 [ MPa ] [ MPa ] [ % ] [ % ] Room
temperature 815 880 14 . 0 40 150 °C 635 730 17 . 6 48 The failure analysis of
the ...
Table 2 : Tensile tests on round specimens , axial test direction ( all base material
, Ø = 3 mm ) . Test temperature Roo . 2 Rm A5 [ MPa ] [ MPa ] [ % ] [ % ] Room
temperature 815 880 14 . 0 40 150 °C 635 730 17 . 6 48 The failure analysis of
the ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
I | 7 |
OMAE99MAT2041 | 9 |
Copyright | |
29 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment axial backing base behavior bending brace Charpy compared components composite condition Conference Copyright crack critical CTOD curve cyclic defects deposition depth determined developed distribution effect element energy Engineering equations evaluated experimental factors failure fatigue ferrite fiber Figure fire flux fracture toughness function geometry given heat input impact improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten obtained Offshore operation parameters performance phase pipe plate pool prediction present pressure procedure production properties range ratio reduced region requirements residual stress risers short shown shows SINTAP specimens speed standard steel strain strength structures surface Table temperature tensile thickness titanium tube underwater values weld metal wire yield
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3 |
| Contributors | OMAE Conference Committee, American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division, American Society of Mechanical Engineers |
| Publisher | American Society of Mechanical Engineers, 2000 |
| Original from | the University of Michigan |
| Digitized | 3 Dec 2007 |
| Export Citation | BiBTeX EndNote RefMan |