... condition , and it is almost impossible to use any active lighting system to capture clear welding arc image . Special optical band pass filter , which main transparency wave length of 953nm and band pass width of 13nm , was used to try ...
... condition , and it is almost impossible to use any active lighting system to capture clear welding arc image . Special optical band pass filter , which main transparency wave length of 953nm and band pass width of 13nm , was used to try ...
Page 319
... condition tested at -20 ° C Table 5 shows the results from Charpy tests , performed at - 55 ° C and at -85 ° C . MECHANICAL PROPERTIES The results of the tensile and the hardness tests of the specimens in both the " as received " condition ...
... condition tested at -20 ° C Table 5 shows the results from Charpy tests , performed at - 55 ° C and at -85 ° C . MECHANICAL PROPERTIES The results of the tensile and the hardness tests of the specimens in both the " as received " condition ...
Page 320
... condition ; ( b ) heat treated condition · The delamination reduces the triaxiality of stress at the crack tip ; with the specimen acting as if it was a series of fine specimens , under plane stress conditions , instead of a thick ...
... condition ; ( b ) heat treated condition · The delamination reduces the triaxiality of stress at the crack tip ; with the specimen acting as if it was a series of fine specimens , under plane stress conditions , instead of a thick ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield