... deformation and cleavage occurred across the M - A and the broken M - A were observed . It was also found that there was no interfacial fracture between M - A and matrix . For the specimen which was not sub - zero treated , the heavy ...
... deformation and cleavage occurred across the M - A and the broken M - A were observed . It was also found that there was no interfacial fracture between M - A and matrix . For the specimen which was not sub - zero treated , the heavy ...
Page 279
... deformation of matrix for relieving the high stress was not easy and therefore the matrix cleaved . However at room temperature , the plastic deformation of matrix easily occurred and relieved the high stress . REFERENCES Fultz , B ...
... deformation of matrix for relieving the high stress was not easy and therefore the matrix cleaved . However at room temperature , the plastic deformation of matrix easily occurred and relieved the high stress . REFERENCES Fultz , B ...
Page 292
... deformation of the matrix also relaxes stress concentration at the brittle microphase and suppresses the microcrack formation . The ferrite matrix of nickel containing steel is easily deformed plastically even at low temperature with ...
... deformation of the matrix also relaxes stress concentration at the brittle microphase and suppresses the microcrack formation . The ferrite matrix of nickel containing steel is easily deformed plastically even at low temperature with ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength