Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 17
Page 138
... Fatigue test specimens were removed from each welded plate by laser cutting ... cracks were observed visually at two weld toes as well . The average weld ... fatigue data generated in this project can be compared both to standard design ...
... Fatigue test specimens were removed from each welded plate by laser cutting ... cracks were observed visually at two weld toes as well . The average weld ... fatigue data generated in this project can be compared both to standard design ...
Page 150
... fatigue cracks were predominately initiated in the consumable ring although failure in the base material should be ... fatigue crack initiation could be attributed to weld defects . There was strong evidence that fatigue failure was ...
... fatigue cracks were predominately initiated in the consumable ring although failure in the base material should be ... fatigue crack initiation could be attributed to weld defects . There was strong evidence that fatigue failure was ...
Page 163
... fatigue crack initiation was carried out visually by spraying white spirit on the surface of the joint . Initial cracks could be detected by observing the pumping of liquid in and out of the crack in phase with the loading . In most of ...
... fatigue crack initiation was carried out visually by spraying white spirit on the surface of the joint . Initial cracks could be detected by observing the pumping of liquid in and out of the crack in phase with the loading . In most of ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength