Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 17
Page 66
Fig . 5 Typical eddy current flow on molten pool . ( a ) No shielding ( c ) Atal (. ( a ) typical image , ( b ) peak image , slag locus ( c ) mean image , ( d ) subtracted image ( b ) - ( c ) . Small Eddy current flow patterns was ...
Fig . 5 Typical eddy current flow on molten pool . ( a ) No shielding ( c ) Atal (. ( a ) typical image , ( b ) peak image , slag locus ( c ) mean image , ( d ) subtracted image ( b ) - ( c ) . Small Eddy current flow patterns was ...
Page 90
... flow rate ( L / min ) 100 - 150 10-20 ( b ) water flow rate ( L / min ) 20-25 Figure 1 shows fixed type copper backing strips . Long copper block with girder for Uranami bead and two drilled bores for cooling water was used for first ...
... flow rate ( L / min ) 100 - 150 10-20 ( b ) water flow rate ( L / min ) 20-25 Figure 1 shows fixed type copper backing strips . Long copper block with girder for Uranami bead and two drilled bores for cooling water was used for first ...
Page 96
... flow rate , water curtain flow rate , wire , and nozzle - work distance were 200A , 28V , 13cm / min , 80 % Ar + 20 % CO2 , 130L / min , 25L / min , MX - 100 flux cored wire , and 7mm , respectively . CONCLUSION Fundamental experiment ...
... flow rate , water curtain flow rate , wire , and nozzle - work distance were 200A , 28V , 13cm / min , 80 % Ar + 20 % CO2 , 130L / min , 25L / min , MX - 100 flux cored wire , and 7mm , respectively . CONCLUSION Fundamental experiment ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength