Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 9
Page 247
... line pipes is growing in gas transportation and the practical strength of line pipes is extending to the X80 grade ... fusion line for a conventional X80 line pipe . The Charpy absorbed energy decreased with the increase in wall ...
... line pipes is growing in gas transportation and the practical strength of line pipes is extending to the X80 grade ... fusion line for a conventional X80 line pipe . The Charpy absorbed energy decreased with the increase in wall ...
Page 251
... fusion line at -30 ° C , J 300 B.M. ( W.M Developed X80 200 100 Conventional X80 0 0 10 20 Wall thickness , mm 30 40 Fig . 7 Relation between wall thickness and Charpy absorbed energy of longitudinal seam weld fusion line ( external ) ...
... fusion line at -30 ° C , J 300 B.M. ( W.M Developed X80 200 100 Conventional X80 0 0 10 20 Wall thickness , mm 30 40 Fig . 7 Relation between wall thickness and Charpy absorbed energy of longitudinal seam weld fusion line ( external ) ...
Page 253
Fusion line + 2 mm Temperature , ° C Fig.11 Charpy impact test result of SMAW welds for simulation of girth ... Fusion line SMAW : E8010G 4,0 50 300 250 GMAW : ER70S - 6 9- . Charpy absorbed energy , J Shear area ...
Fusion line + 2 mm Temperature , ° C Fig.11 Charpy impact test result of SMAW welds for simulation of girth ... Fusion line SMAW : E8010G 4,0 50 300 250 GMAW : ER70S - 6 9- . Charpy absorbed energy , J Shear area ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
OMAE99MAT2042 | 19 |
Copyright | |
27 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding weld metal weld pool weld toe welded joints welding conditions wet welding wide plate wire yield strength