Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 36
Page 137
... heat input , and larger weld toe radii for the high heat input plate corresponded to an additional increase in fatigue performance beyond the other GTAW procedures . These limited results demonstrate the important effects of weld ...
... heat input , and larger weld toe radii for the high heat input plate corresponded to an additional increase in fatigue performance beyond the other GTAW procedures . These limited results demonstrate the important effects of weld ...
Page 138
... heat input tests , two specimens failed from locations other than the weld toe , from a plate stamp impression near ... heat input plates are shown in Figure 5. Both the average values and the scatter plots of the weld toe geometry data ...
... heat input tests , two specimens failed from locations other than the weld toe , from a plate stamp impression near ... heat input plates are shown in Figure 5. Both the average values and the scatter plots of the weld toe geometry data ...
Page 139
... heat input welds . The geometry readings are also correlated to fatigue performance . The high heat input panel , with the largest angles and radii , gave the best fatigue performance , with a run - out to 5 million cycles at 200 N ...
... heat input welds . The geometry readings are also correlated to fatigue performance . The high heat input panel , with the largest angles and radii , gave the best fatigue performance , with a run - out to 5 million cycles at 200 N ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield