... Mechanical properties of the X80 steel plate produced . Thick -ness YS TS EI . YR Cv at -40 ° C CVN50 % ( mm ) ( MPa ) ( MPa ) ( % ) ( % ) ( J / mm2 ) 19.1 572 696 39 82 6.0 ( 481J ) 25.4 564 692 46 82 5.6 ( 448J ) FATT ( ° C ) -110 ...
... Mechanical properties of the X80 steel plate produced . Thick -ness YS TS EI . YR Cv at -40 ° C CVN50 % ( mm ) ( MPa ) ( MPa ) ( % ) ( % ) ( J / mm2 ) 19.1 572 696 39 82 6.0 ( 481J ) 25.4 564 692 46 82 5.6 ( 448J ) FATT ( ° C ) -110 ...
Page 268
... mechanical properties , those of the X80 ( II ) steel at -5 ° C were used as a basis ( yield stress σ , = 583 MPa ( 0.2 % proof stress ) , tensile strength 6 , 711 MPa , yield ratio YR = 0 , / 6 , -0.82 , uniform t = 25 Surface crack 20 ...
... mechanical properties , those of the X80 ( II ) steel at -5 ° C were used as a basis ( yield stress σ , = 583 MPa ( 0.2 % proof stress ) , tensile strength 6 , 711 MPa , yield ratio YR = 0 , / 6 , -0.82 , uniform t = 25 Surface crack 20 ...
Page 289
... mechanical properties of base metal , and HAZ toughness . It mainly consist of control of amount of Cu , Ni , Nb in order to control the HAZ microstructure and improve strength of base metal . Addition of small amount of Nb content is ...
... mechanical properties of base metal , and HAZ toughness . It mainly consist of control of amount of Cu , Ni , Nb in order to control the HAZ microstructure and improve strength of base metal . Addition of small amount of Nb content is ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength