Page 104
... microstructure and causes decreased strength and toughness . The microstructure of wet welds consists mainly of coarse primary ferrite ( PF ) and ferrite with aligned carbides ( FS ) depths ( Ibarra et al 1987 ) . In contrast , surface ...
... microstructure and causes decreased strength and toughness . The microstructure of wet welds consists mainly of coarse primary ferrite ( PF ) and ferrite with aligned carbides ( FS ) depths ( Ibarra et al 1987 ) . In contrast , surface ...
Page 106
... microstructures due to its resistance to cleavage fracture . Figure 8 shows the difference in microstructure produced with the addition of titanium and boron at 140 ft . V - GROOVE WELDS The formulations 1F3 , 2F3 , 3F3 , and 4F2 were ...
... microstructures due to its resistance to cleavage fracture . Figure 8 shows the difference in microstructure produced with the addition of titanium and boron at 140 ft . V - GROOVE WELDS The formulations 1F3 , 2F3 , 3F3 , and 4F2 were ...
Page 286
... microstructure region in the Figure . This difference in the microstructure among the weld metals is probably caused by the difference in the dilution shown in Fig . 1. Thus , it should be noted that the application of different welding ...
... microstructure region in the Figure . This difference in the microstructure among the weld metals is probably caused by the difference in the dilution shown in Fig . 1. Thus , it should be noted that the application of different welding ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength