... plate surface condition , and manual welding of GTAW fillet welds on steel plates was studied . Welding was done in the flat position with a vertical torch using ER70S - 2 filler metal . Fatigue testing used cyclic axial tension load ...
... plate surface condition , and manual welding of GTAW fillet welds on steel plates was studied . Welding was done in the flat position with a vertical torch using ER70S - 2 filler metal . Fatigue testing used cyclic axial tension load ...
Page 138
... plate by laser cutting remote from the attachment followed by saw cutting through the attachment region . The ... plate . For the minimally surface treated plate , 20 cross - sections were examined . For the other plates , where less ...
... plate by laser cutting remote from the attachment followed by saw cutting through the attachment region . The ... plate . For the minimally surface treated plate , 20 cross - sections were examined . For the other plates , where less ...
Page 245
... Plate - 15mm Plate 25mm Plate 1.2 FIG . 10 Predicted Pellini NDTT Requirements for Crack Arrest at 0 ° C Thus , the Pellini NDTT values for as - rolled ship plate are generally too high to satisfy the maximum NDTT criterion of -18 ° C ...
... Plate - 15mm Plate 25mm Plate 1.2 FIG . 10 Predicted Pellini NDTT Requirements for Crack Arrest at 0 ° C Thus , the Pellini NDTT values for as - rolled ship plate are generally too high to satisfy the maximum NDTT criterion of -18 ° C ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield