Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 49
Page 38
... region of the plate and compression in the outer regions . The maximum residual stress was 57 % of the yield strength . The second series of tests consisted of two pairs of welded specimens , each pair consisting of an as - welded and a ...
... region of the plate and compression in the outer regions . The maximum residual stress was 57 % of the yield strength . The second series of tests consisted of two pairs of welded specimens , each pair consisting of an as - welded and a ...
Page 64
... region . White mark on the molten metal near center region is reflected image of lighting . Figure 2 ( f ) shows subtracted arc image of ( b ) . Brightness of the image is described in blue . Color on molten metal in figure 2 ( b ) is ...
... region . White mark on the molten metal near center region is reflected image of lighting . Figure 2 ( f ) shows subtracted arc image of ( b ) . Brightness of the image is described in blue . Color on molten metal in figure 2 ( b ) is ...
Page 156
... region was as recommended by the Department of Energy ( 1984 ) . With regard to Fig . 3 , the R ratio is defined as ... region using the polynomial function obtained . 5. Perform a linear extrapolation to the weld toe or the weld root of ...
... region was as recommended by the Department of Energy ( 1984 ) . With regard to Fig . 3 , the R ratio is defined as ... region using the polynomial function obtained . 5. Perform a linear extrapolation to the weld toe or the weld root of ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield