Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 13
Page 67
... SHIELDING GAS AND WIRE ELECTRODE ON MIG Welding Y.OGAWA and T.MORITA Shikoku National Industrial Research Institute Takamatsu , Japan ( b ) CO2 = 20 L / min (. OMAE99 / MAT - 2203 ABSTRACT Welding arc behavior is much influenced by used ...
... SHIELDING GAS AND WIRE ELECTRODE ON MIG Welding Y.OGAWA and T.MORITA Shikoku National Industrial Research Institute Takamatsu , Japan ( b ) CO2 = 20 L / min (. OMAE99 / MAT - 2203 ABSTRACT Welding arc behavior is much influenced by used ...
Page 68
... welding machine moved during welding , then molten pool moved with welding speed . Inverter Auto 350 by Daihen Co. was used as power source . And , the wire was woven to fulfill molten metal in the groove . The effect of shielding gas ...
... welding machine moved during welding , then molten pool moved with welding speed . Inverter Auto 350 by Daihen Co. was used as power source . And , the wire was woven to fulfill molten metal in the groove . The effect of shielding gas ...
Page 73
... shielding gas and wire on arc welding condition . REFERENCES Welding arc behavior was observed by interference ... shielding gas and wire electrode was discussed in details . Used shielding gases were argon , argon rich CO2 gas ( Ar80 ...
... shielding gas and wire on arc welding condition . REFERENCES Welding arc behavior was observed by interference ... shielding gas and wire electrode was discussed in details . Used shielding gases were argon , argon rich CO2 gas ( Ar80 ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield