Page 240
... ship results in strain rate in the mid - ships section of around 2 x 103 = 100 MPa in 0.25s . By extrapolating measured values it may deduced that strain rates of around 2 x 102 s11 might be achieved under extreme conditions in the deck ...
... ship results in strain rate in the mid - ships section of around 2 x 103 = 100 MPa in 0.25s . By extrapolating measured values it may deduced that strain rates of around 2 x 102 s11 might be achieved under extreme conditions in the deck ...
Page 245
... ship plate are generally too high to satisfy the maximum NDTT criterion of -18 ° C for primary structure in ships and are probably insufficient to arrest running cracks in ship structures . The probability of achieving such a value or ...
... ship plate are generally too high to satisfy the maximum NDTT criterion of -18 ° C for primary structure in ships and are probably insufficient to arrest running cracks in ship structures . The probability of achieving such a value or ...
Page 246
... ship . The principal concern is therefore the ability of Grade A plate to arrest an initiated and fast - running crack . The reviewed literature suggests that the crack arrest ability of Grade A plate is poor and probably inadequate in ...
... ship . The principal concern is therefore the ability of Grade A plate to arrest an initiated and fast - running crack . The reviewed literature suggests that the crack arrest ability of Grade A plate is poor and probably inadequate in ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength