... shown in Fig . 8 for over - matched specimens , and in Fig . 9 for undermatched specimens . Construc- tion of the failure assessment curve for mis - match requires knowledge of the mismatch yield loads for mismatched specimens , FM ...
... shown in Fig . 8 for over - matched specimens , and in Fig . 9 for undermatched specimens . Construc- tion of the failure assessment curve for mis - match requires knowledge of the mismatch yield loads for mismatched specimens , FM ...
Page 106
... shown in Figure 6. The microstructures were composed mainly of primary ferrite ( PF ) , and ferrite with second phase ( FS ) . All of the microstructures contained approximately 15-20 percent acicular ferrite . Figure 6 shows a strong ...
... shown in Figure 6. The microstructures were composed mainly of primary ferrite ( PF ) , and ferrite with second phase ( FS ) . All of the microstructures contained approximately 15-20 percent acicular ferrite . Figure 6 shows a strong ...
Page 313
Charpy impact test results are shown in Fig.6 to 10 and CTOD test results are shown in Fig . 11.Test results at all the locations completely satisfied the target in as - welded condition , the minimum absorbed energy of Charpy impact ...
Charpy impact test results are shown in Fig.6 to 10 and CTOD test results are shown in Fig . 11.Test results at all the locations completely satisfied the target in as - welded condition , the minimum absorbed energy of Charpy impact ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength