Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 3American Society of Mechanical Engineers, 2000 - Arctic regions |
From inside the book
Results 1-3 of 79
Page 28
Test temperature = -65 ° C Yield strength at −65 ° C = 409MPa RESULTS The results from the mml procedure are summarised in Table 1 . The fracture toughness distributions predicted from each of the three steps are compared with the ...
Test temperature = -65 ° C Yield strength at −65 ° C = 409MPa RESULTS The results from the mml procedure are summarised in Table 1 . The fracture toughness distributions predicted from each of the three steps are compared with the ...
Page 259
... Results of drop - weight test Test 1 piece Location Direction TNDT type ( °C ) P - 2 subsurface T No 324 5 % + aging 310 291 305 258 -135 231 -125 Surface 1/21 L L -120 -90 10 % + aging 298 No 244 206 -105 Table 7 Results of Y - groove ...
... Results of drop - weight test Test 1 piece Location Direction TNDT type ( °C ) P - 2 subsurface T No 324 5 % + aging 310 291 305 258 -135 231 -125 Surface 1/21 L L -120 -90 10 % + aging 298 No 244 206 -105 Table 7 Results of Y - groove ...
Page 266
... test results X80 ( 11 ) steel welds at -5 ° C Undermatch E∞ Ex 1.0 | X80 ( 11 ) Vg strain , respectively , C is the ... test tempera- ture . Elements used in the FE - analysis were 8 - node isoparametric elements with 8 - Gaussian ...
... test results X80 ( 11 ) steel welds at -5 ° C Undermatch E∞ Ex 1.0 | X80 ( 11 ) Vg strain , respectively , C is the ... test tempera- ture . Elements used in the FE - analysis were 8 - node isoparametric elements with 8 - Gaussian ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
absorbed energy analysis Arctic Engineering July ASME assessment austenite base metal behavior bending brace CGHAZ Charpy impact Charpy impact test chord component composite material Conference On Offshore copper backing Copyright CTOD value curve cyclic defects developed dynamic effect Engineering July 11-16 equations equivalent CTOD evaluated fatigue tests ferrite fiber fire flux fracture toughness geometry GMAW GTAW HAZ toughness heat input increase intumescents iteration matrix maximum mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters passive fire protection porosity procedure Proceedings of OMAE99 PWHT ratio requirements residual stress risers S-N curve SCFEX shielding gas short circuiting SINTAP specimens standards steel plates strain stress intensity submerged arc welding surface Table temperature test results thickness titanium underwater welding Weibull stress weld metal weld pool weld toe welded joints wet welding wide plate wire yield strength