Page 42
... welding standard offshore structural steels ( 355 MPa yield strength ) and the higher strength steels ( 420-450 MPa yield strength ) became single and / or tandem submerged arc welding with or without metal powder additions . In more ...
... welding standard offshore structural steels ( 355 MPa yield strength ) and the higher strength steels ( 420-450 MPa yield strength ) became single and / or tandem submerged arc welding with or without metal powder additions . In more ...
Page 50
... weld metal toughness can be obtained for welds deposited using identical welding consumables with 4/5 wire systems compared to 3 wire systems . Weld Metal Microstructure The two pass submerged arc welding of line pipe results in weld ...
... weld metal toughness can be obtained for welds deposited using identical welding consumables with 4/5 wire systems compared to 3 wire systems . Weld Metal Microstructure The two pass submerged arc welding of line pipe results in weld ...
Page 105
the V - groove welds in addition to the other analyses which were performed on the BOP welds . All - weld - metal tensile tests were performed on each V - groove weld with a 1⁄4 inch round bar . Five full- size bars were taken from each ...
the V - groove welds in addition to the other analyses which were performed on the BOP welds . All - weld - metal tensile tests were performed on each V - groove weld with a 1⁄4 inch round bar . Five full- size bars were taken from each ...
Contents
STRUCTURAL INTEGRITY PROCEDURES FOR EUROPE SINTAP | 1 |
OMAE99MAT2041 | 9 |
Development of the SINTAP Failure Assessment Diagrams for Compatibility With | 19 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applications approach ASME assessment base behavior bending CGHAZ Charpy compared component composite condition Conference Copyright crack critical CTOD curve defects deposition depth determined developed distribution dynamic effect element energy Engineering equations equivalent evaluated factors failure fatigue ferrite Figure fire fracture toughness function geometry given hardness heat input impact important improve increase initiation International joints length limit loading lower material matrix maximum mean measured mechanical method microstructure molten observed obtained offshore operating parameters performance phase pipe plate prediction present pressure procedure production properties protection range ratio reduced region requirements residual stress respectively risers safety ship shown shows specimens standards steel strain strength structures surface Table temperature tensile thickness values weld metal welded joints wire yield