Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 12, Part 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 78
Page 559
... calculated by the simple beam theory . Therefore , the local translational displacement in the direction of the brace axis is 8 = ( Ao - Vo ) sine P. MII Mor P = + Ab + Ac + Ad ) - vo ] sine ( 7 ) brace I Mo brace II Let the total ...
... calculated by the simple beam theory . Therefore , the local translational displacement in the direction of the brace axis is 8 = ( Ao - Vo ) sine P. MII Mor P = + Ab + Ac + Ad ) - vo ] sine ( 7 ) brace I Mo brace II Let the total ...
Page 613
... calculated and plotted against weld metal strength overmatch , as shown in Fig . 7. Linear regression of this data gave a correlation coefficient of 0.84 and a standard deviation on overmatch of about 70 N / mm2 . Considering the ...
... calculated and plotted against weld metal strength overmatch , as shown in Fig . 7. Linear regression of this data gave a correlation coefficient of 0.84 and a standard deviation on overmatch of about 70 N / mm2 . Considering the ...
Page 618
... CALCULATED WITH MEASURED AS A FUNCTION OF CALCULATED Sr FOR A HAZ NOTCHED WIDE PLATE TEST HAVING MATCHING STRENGTH WELD METAL . LEVEL 2 FAD 1.60 0 Measured 1.40 A Calculated 1.20 . 1.00 0.80 Failure 0.60 No Failure 0.40 0.20 0.00 0.0 ...
... CALCULATED WITH MEASURED AS A FUNCTION OF CALCULATED Sr FOR A HAZ NOTCHED WIDE PLATE TEST HAVING MATCHING STRENGTH WELD METAL . LEVEL 2 FAD 1.60 0 Measured 1.40 A Calculated 1.20 . 1.00 0.80 Failure 0.60 No Failure 0.40 0.20 0.00 0.0 ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength