... composite pipe has been considered a viable alternative to carbon steel , stainless steel and copper- nickel pipe in sea water applications . The most obvious benefit of utilizing composite pipe for offshore applications is its ...
... composite pipe has been considered a viable alternative to carbon steel , stainless steel and copper- nickel pipe in sea water applications . The most obvious benefit of utilizing composite pipe for offshore applications is its ...
Page 326
The Composite Pipe Industry suffers from a severe lack of standardization . Composite Pipe is known in various countries as GRP , FRP , RTRP , or merely FIBERGLASS PIPE . A distinction must be made between the use of composite pipe in ...
The Composite Pipe Industry suffers from a severe lack of standardization . Composite Pipe is known in various countries as GRP , FRP , RTRP , or merely FIBERGLASS PIPE . A distinction must be made between the use of composite pipe in ...
Page 331
... composite pipe tested . While the epoxy and vinyl ester epoxy samples caught fire , the phenolic based samples would not ignite ( in fact , these pipe samples often extinguished the support flame which was used to burn the samples ) ...
... composite pipe tested . While the epoxy and vinyl ester epoxy samples caught fire , the phenolic based samples would not ignite ( in fact , these pipe samples often extinguished the support flame which was used to burn the samples ) ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength