... corrosion resistance of austenite , but with improved stress corrosion cracking resistance and strength associate with ferrite . Carefully controlled manufacturing techniques are employed to produce this combination in roughly equal ...
... corrosion resistance of austenite , but with improved stress corrosion cracking resistance and strength associate with ferrite . Carefully controlled manufacturing techniques are employed to produce this combination in roughly equal ...
Page 95
... corrosion resistance more effectively than austenite induced by nickel . Corrosion Resistance The increased nitrogen and austenite levels are reflected in the results of the corrosion resistance tests . These are shown as a series of ...
... corrosion resistance more effectively than austenite induced by nickel . Corrosion Resistance The increased nitrogen and austenite levels are reflected in the results of the corrosion resistance tests . These are shown as a series of ...
Page 279
... corroded , and , consequently , had to be changed . Corrosion experts had the evidence that this corrosion was caused by the use of sea water , and , accordingly , had to select an appropriate corrosion resistant material for the ...
... corroded , and , consequently , had to be changed . Corrosion experts had the evidence that this corrosion was caused by the use of sea water , and , accordingly , had to select an appropriate corrosion resistant material for the ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength