Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 12, Part 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 78
Page 116
... electrodes for Part 4 . Southwest Research Center's Joint Industry wet welding electrode developmental program is unique in that it embodies the use of flux cored / externally coated electrodes as opposed to conventional welding electrodes ...
... electrodes for Part 4 . Southwest Research Center's Joint Industry wet welding electrode developmental program is unique in that it embodies the use of flux cored / externally coated electrodes as opposed to conventional welding electrodes ...
Page 121
... electrodes . Table 4. Dry mix composition ( in grams ) of C - series electrode coverings . CC3 CC4 CCS CC6 CC7 CC8 ... electrodes and 1.7 kJ / mm ( 43kJ / in ) and direct current electrode positive ( DCEP ) with the electrodes of the C ...
... electrodes . Table 4. Dry mix composition ( in grams ) of C - series electrode coverings . CC3 CC4 CCS CC6 CC7 CC8 ... electrodes and 1.7 kJ / mm ( 43kJ / in ) and direct current electrode positive ( DCEP ) with the electrodes of the C ...
Page 134
... electrodes even when the weld metal of austenitic and nickel based electrodes is said to be able to sustain high amounts of hydrogen without any Hydrogen Induced Cold Cracking ( HICC ) . It was found in several preliminary tests that ...
... electrodes even when the weld metal of austenitic and nickel based electrodes is said to be able to sustain high amounts of hydrogen without any Hydrogen Induced Cold Cracking ( HICC ) . It was found in several preliminary tests that ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength