Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 12, Part 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 70
Page 189
... fabrication , in terms of the requirement for less stringent welding precautions during fabrication . Five steels of 690MPa nominal yield strength with good toughness and which were available in 50mm thick section were selected for ...
... fabrication , in terms of the requirement for less stringent welding precautions during fabrication . Five steels of 690MPa nominal yield strength with good toughness and which were available in 50mm thick section were selected for ...
Page 193
... Fabrication As discussed previously , a further important aim of the current work was to assess the potential of these steels to be fabricated in the absence of preheat . It has been shown that the modern steels possess an inherent ...
... Fabrication As discussed previously , a further important aim of the current work was to assess the potential of these steels to be fabricated in the absence of preheat . It has been shown that the modern steels possess an inherent ...
Page 255
... fabrication is summarised by fig 7 it can be seen that ring stiffeners , barrelling and offset work points are effectively eliminated in the simple cast steel solution . www Trunnion Nodes all This concept has been further developed ...
... fabrication is summarised by fig 7 it can be seen that ring stiffeners , barrelling and offset work points are effectively eliminated in the simple cast steel solution . www Trunnion Nodes all This concept has been further developed ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength