Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 12, Part 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 81
... weld metal inclusions has been shown to reduce H , refine non- metallic inclusions , and improve weldability ... weld metals produced with them . 25 - mm- thick weldments were produced with HY - 100 plate ( MIL - S- 16216J , 1981 ) and a ...
... weld metal inclusions has been shown to reduce H , refine non- metallic inclusions , and improve weldability ... weld metals produced with them . 25 - mm- thick weldments were produced with HY - 100 plate ( MIL - S- 16216J , 1981 ) and a ...
Page 123
... METAL BORON CONTENT ( ppm ) * * * LELO PETAL TITANIUM CONTENT ( Dom ) Figure 3. Weld metal oxygen dependency on weld metal titanium and boron content in underwater wet welds produced with the A- and B - series electrodes . Effect of ...
... METAL BORON CONTENT ( ppm ) * * * LELO PETAL TITANIUM CONTENT ( Dom ) Figure 3. Weld metal oxygen dependency on weld metal titanium and boron content in underwater wet welds produced with the A- and B - series electrodes . Effect of ...
Page 621
The weld metal yield strength ( all - weld metal round bar specimens ) of weld deposit L varied between 514 MPA at SS and 557 MPa at MT , which is a consequence of the higher cooling rate at mid - thickness . The through - thickness ...
The weld metal yield strength ( all - weld metal round bar specimens ) of weld deposit L varied between 514 MPA at SS and 557 MPa at MT , which is a consequence of the higher cooling rate at mid - thickness . The through - thickness ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength